High RUL bricks
 
 该产品具有荷重软化温度和强度高,热震稳定性好和耐磨性优越的特点,主要用于大中型回转窑高温部位,代替镁铬砖并适用于冶金行业电炉、转炉等主要部位。
These products high RUL good thermal shock resistance, high strength and abrasion resistance, Their main applications are as followings; high temperature zone of large and medium size rotary kilns, substituting magnesite chrome bricks in main part of electric furnace and converter for metallurgical industry.
性能 properties
牌号 Brands

PH-75

PH-80

化学成份 
Chemiacl composition,%

Al2O3%

≥75

≥80

Fe2O3%

≤1.5

≤1.5

显气孔率 Apparent porosity,%

≤20

≤18

体积密度 BD,g/cm3

2.65

2.7

耐压强度 CCS,Mpa

≥70

≥80

荷重软化开始温度 RUL,℃

≥1550

≥1570

重烧线变化 Linear change on reheating(1550℃×3h),%

-0.8~+0.3

-0.8~+0.3

热震稳定性 (900℃水冷)Thermal shock Resistance cycles,≥

≥40

≥40

蓝晶石高铝制品
Kyanite high alumina products

性能 properties
项目 Atam
冶金部下达的宝钢用热风炉砖H24
Al2O3,%
≥60
耐火度 Refractoriness,℃
≥1820
显气孔率 Apparent porosity,%
≤24
耐压强度CCS,Mpa
≥40


红柱石砖

性能 properties
项目 Atam
腊石砖
化学成份 Al2O3,% ≤50
Fe2O3,% ≤1.0
SiO2,% ≥48
体积密度 BD,g/cm3 ≥2.35
常温耐压强度 CCS,Mpa ≥60
显气孔率 Apparent porosity,% ≤22
荷重软化开始温度 RUL,℃ ≥1400
耐火度 Refractoriness,℃ ≥1770

高铝砖
High alumina bricks
 
                                                                                                                                                            【GB2988-87】

高铝砖.jpg

性能 properties
牌号 Brands
一级高铝
二级高铝
三级高铝
LZ-75
LZ-65
LZ-55
LZ-48

Al2O3,≥ %

75
65
55
48

耐火度 Refractoriness,≥,℃

1790
1770
1750

0.2Mpa 荷重软化开始温度 RUL, T0.6,℃≥,℃

1520
1500
1470
1420

重烧线变化
Linear change on reheating,%

1500℃×2h
+0.1
-0.4
-0.4
1450℃×2h

+0.1
-0.4

显气孔率 Apparent porosity,≤ %
23
22
常温耐压强度 CCS,≥Mpa
≥53.9
≥49.0
≥44
≥40

最后更新
热门点击
地 址:中国-申苏浙皖高速长兴西出口1公里处(老318国道9公里处)       Copyright (C) 2004 Zhejiang Xiangfa Refractory Co.,Ltd.  
 服务热线: 0572 - 6011047 / 6011516     传真: 0572 - 6011283     E-mail: hyx@chinarefractory.com     备案序号:浙ICP备05029667号      网站统计
           
点击这里给我发消息
点击这里给我发消息